Melt flow Indexer TMFI-A10 comes in compact structure & attractive design & with high quality performance & reliable results, it can measure (melt mass flow rate) MFR, (melt volume flow rate) MVR of the sample, melt density of thermos-resins. Adopted with standard module combination structure, it can upgrade and changed the type directly, with accuracy of the results. It is designed in accordance with latest ISO international standards.
| Measuring range | 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density) |
| Measuring rate | 0.001 S |
| Temperature range | 50 to 400°C |
| Temperature precision | ± 0.5°C |
| Resolution | 0.1°C |
| Accuracy | 0.005 |
| Weights | 0.325 kg, 1.2 kg, 2.16 kg, 3.8 kg, 10.0 kg, 12.5 kg, 21.6 kg |
| Material canister dimension | Nil |
| Piston dimension | Nil |
| Dimension | 600×400×500 mm |
| Net weight | 85 kg |
| Gross weight | 98 kg |
| Power | 550 W |
| Power supply | 220/ 110 V, 50/60 Hz |
- LCD digital display
- Can perform three measurements: MFR/MVR/ Density
- Can cut the material manually or automatically
- Adopted with Microprocessor PID temperature controller
- Cleaning & calibration accessories for reliable performance
- Easy to use/operate
Melt flow indexer is used to determine the melt mass-flow (MFR), the melt volume-flow rate (MFV) and the melt density of thermos-resins, polycarbonates, nylon & plastic material.
Plastic Testing Instruments
Lasting adhesive tester TLAT-A11
- Standard roller
- 2000 ± 50 g
- Testing stations
- 6
- Dimension (L*W*H) tester
- 650×210×550 mm (6 stations)
Vicat softening temperature & HDT machine TVHT-A10
- Operating temperature
- Ambient temperature to 300°C
- Heating rate
- 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min)
- Maximum temp. error with heating speed
- ± 5°C under 50°C/ h, ± 1°C under 120°C/ h
Primary adhesive tester TPAT-A10
- Inclined adjustable angle
- 0 to 40°
- Panel width
- 120 mm
- Test area width
- 80 mm
Paper Testing Instruments
Ink rubber tester TP-F10
- Sample size (L*B)
- 230×50 mm (can join short samples together)
- Rub pressure
- 20 ± 0.2 N
- Friction speed
- 43 times / min
Water absorption tester TP-C20
- Measurement range
- 0 to 200 mm
- Specimen size
- 15×250 mm
- Division value
- 1 mm
Coefficient of friction tester TP-D10
- Measurement range
- 0.01 to 10 N
- Slider weight
- 200 g
- Slider size
- 63×63 mm
Tensile Stiffness Tester TP-B10
- Sample (size) length
- 38×70 mm
- Measuring range
- (1-500) mN.m (divided into 7 small ranges)
- Indication error
- 0.02
Rubber Testing Instruments
Mooney viscometer TMV-A10
- Control temperature range
- Normal temperature to 200°C
- Temperature display resolution
- 0.01°C
- Temperature control accuracy
- ± 0.3°
Three roll mill machine TRMM-A10
- Mixed capacity
- 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg
- Temperature range
- RT to 300°C
- Temperature control system
- PID control
Rubber Low Temperature Brittleness Tester TRBT-A11
- Temperature control range
- Room temperature to -70 ℃ (room temperature ≤ 25 ℃）
- Temperature accuracy
- ± 0.3 ℃
- Impact speed
- 0℃ to -30℃ around 2.5 ℃/min '-30℃ to -40℃ around 2.5 ℃/min '-40℃ to -70℃ around 2.0 ℃/min
Rubber low temperature brittleness tester TRBT-A10
- Temperature range
- -60°C to 0°C
- Temperature accuracy
- ± 0.5°C
- Impact speed
- 2 m/s ± 0.2 m/s
NDT Testing Instruments
Portable Vibration Calibrator LPVC-A10
- Frequency (continually adjustable)
- 10 Hz to1280 Hz + 0.01 %
- Amplitude acceleration ( at 30m/s2 pk )
- 40 Hz to 320 Hz + 0.3 dB + 1 digit
- Amplitude velocity ( at 25mm / sec pk )
- 40 Hz to 320 Hz + 0.5dB +1 digit
Digital Brinell hardness Tester TDBH-A10
- Test force
- 612.5 N, 980 N, 1225 N
- Brinell hardness test
- 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
- Hardness measuring area
- 8 to 650 HBW (hard metals steel ball)
Rockwell hardness meter TRHM-A11
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 1 to 30 S
Rockwell hardness meter TRHM-A10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 0 to 30 S
Other Testing Instruments